Evaluation of Surface Characteristics of Denture Base Using Organic-Inorganic Hybrid Coating: An SEM Study

Ali Abbas Jafari, Mohammad Hossein Lotfi-Kamran, Mahin Ghafoorzadeh, Sayed Mehrzad Shaddel

Abstract


Abstract:

Statement of Problem: Despite the numerous positive features of acrylic denture base, there are a number of undeniable associated disadvantages. The properties of denture base have been improved through various interventions including application of different types of filler and coatings.

Objectives: This study aimed to evaluate the surface roughness, thickness and coating quality of organic-inorganic coating on the denture base through scanning electron microscopy. Moreover, the colour change was evaluated visually.

Materials and Methods: The organic-inorganic hybrid coatings were prepared. Acrylic discs of 10×10 mm were fabricated. The test discs were dipped in the hybrid coating and cured. In order to evaluate the surface roughness and coating thickness, the surface and cross-section of the samples in both coated and control groups were subjected to scanning electron microscopy. The colour change and transparency were visually evaluated with naked eyes. The data were statistically analyzed by student’s t test.

Results: The hybrid materials perfectly covered all the surfaces of acrylic resin and established proper thickness. The coated group seemed smoother and flatter than the control group; however, the difference was not statistically significant ( for all parameters p > 0.05). It was quite a thin coating and no perceptible colour change was observed.

Conclusions: The hybrid coating maintained good binding, caused no noticeable discoloration, and thoroughly covered the acrylic resin surface with uniform delicate thickness. It also slightly improved the acrylic resin surface roughness.

Key words: Denture Base, Hybrid Coating, Surface Roughness, Scanning Electron Microscopy


Full Text:

PDF

Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution 3.0 License.

pISSN :2383-3971              eISSN :2383-398X